This thin transparent organic coating offers additional corrosion protection, increases protection against fingerprints and improves sliding characteristics during forming operations. It can be used as a primer coat for subsequent painting.
Within our range of metallic coated products, Easyfilm® is an environmentally friendly, chromate-free thin organic coating (TOC) continuously applied double-sided on the whole range of electrogalvanised steel, hot dip galvanised steel, galfan, Magnelis®, Alusi® and Alupur®. Easyfilm® complies with current European legislation banning the use of hazardous substances such as hexavalent chromium, specifically the Restriction of the Use of Certain Hazardous Substances in Electrical and Electronic Equipment and the End-of-Life Vehicles directives.
Easyfilm® has a dry appearance. Its essential role during a period of six months starting from the date on which the product becomes available at the manufacturer's works is to:
The applications of Easyfilm® are extremely varied, due to the range of properties and advantages available. They include:
These thin organic coatings can be applied to the following range of ArcelorMittal metallic coated steels:
Thickness (mm) | Min width | Easyfilm® E |
---|---|---|
Max width | ||
0.40 ≤ th < 1.60 | 600 | 1830 |
Thickness (mm) | Min width | Easyfilm® E |
---|---|---|
Max width | ||
0.30 ≤ th < 3.00 | 800 | 1650 |
Thickness (mm) | Min width | Easyfilm® E |
---|---|---|
Max width | ||
0.25 ≤ th < 3.00 | 800 | 1500 |
Thickness (mm) | Min width | Easyfilm® E |
---|---|---|
Max width | ||
0.45 ≤ th < 2.00 | 600 | 1700 |
Thickness (mm) | Min width | Easyfilm® E |
---|---|---|
Max width | ||
0.30 ≤ th < 3.00 | 750 | 1525 |
Thickness (mm) | Min width | Easyfilm® E |
---|---|---|
Max width | ||
0.55 ≤ th < 2.00 | 700 | 1500 |
Performance
Easyfilm® E | |||
---|---|---|---|
Surface protection | Salt spray test corrosion resistance (1) | Electrogalvanised steel | > 50 hours |
Hot dip galvanised steel | > 100 hours | ||
Galfan | > 150 hours | ||
Magnelis® | > 500 hours | ||
Alusi® | |||
Alupur® | |||
Humidity cabinet corrosion resistance (2) | > 500 hours (21 cycles) | ||
Formability | Friction coefficient | µd < 0.15 | |
Weldability | Weldability range | ∆ l > 1 kA | |
Aspect | Anti-fingerprint performance | ∆ E < 2 | |
Electrical conductivity | R < 50 Ω.cm² (for EZ 25/25) | ||
Recommended maximum peak temperature | 200°C | ||
Resistance to degreasing | Thin organic coating weight loss (pH 10, 60°C, 120 s) | < 10% | |
Paintability (3) | Dry paint adhesion | 0 (4) | |
Wet paint adhesion (500 hours humidity cabinet) | 0-2 (4) | ||
Delamination on scratching (120 hours salt spray test) | < 3 mm | ||
Impact test | 0 paint adhesion loss up to 10 J |
(1) Resistance to salt spray test according to ISO 7253/DIN 50021 (evaluation: number of hours before maximum 5% white or black rust appears on the metallic coating)
(2) Resistance to humidity cabinet test according to DIN 50017 (evaluation: number of hours before maximum 1% white or black rust appears on the metallic coating)
(3) Indicative results (tested with two reference paints)
(4) Paint adhesion on a grid; maximum permissible rating is 2 (0 = good adhesion, 5 = poor adhesion) (rating according to ISO 2409)